PVC Shrink Film / Calendered PVC Shrink Film / PETG Shrink Film

• Customization: Available
• Material: PVC
• Usage: Packaging Film
• Model NO.: LQ-SF
• Type: Shrink Film

Product Description

PVC shrink film

 

PROPERTY		TEST METHOD	UNIT	STANDARD
WIDTH		/	MM	(+)6
THICKNESS		ASTM D 374	MIC	(±)3
TENSILE STRENGTH	MD	ASTM D 882	Mpa	>=42.0
	TD			>=150.0
ELONGATION	MD	ASTM D 882	KN/M	>=350.0
	TD			>=60.0
HEAT SHRINKAGE	MD	ASTM D 1204 95ºC/10SEC	%	2
	TD			>=50
C.O.F(IN/OUT)	µs/µk	ASTM D 1984E	--	0.41/0.4
WETTING TENSION		ASTM D 2587	mN/m	40

Note:Please keep the temperature below 25ºC dry warehouse.

CALENDERED PVC SHRINK FILM
 

CALENDERED PVC Shrink film is made by extrusion, calender, stretch and slitting. It is high shrinkage percentage, good transparent and flatness, no wrinkles after shrink. Suit to high-speed automated machine printing, widely applied in hot shrink printing label. The thickness is 35-75 micron, max stretch width is 3600mm.

Properties				Units	Value
	Thickness tolerance			micron	±2.5
	Width tolerance			mm	±2
	Weight tolerance			Kg/Roll	±5%
	Density			g/cm2	1.36
	Haze			%	≤3
Tensile strength			MD	Mpa	≥55
			TD		≥125
Elongation at break			MD	%	≥185
			TD		≥45
Shrinkage		MD	100 ºC	%	0-5
		TD	100 ºC		58-60
	Thickness			micron	50
	Width			mm	400 - 1300
	Shrinkage			-	No wrinkles after shrink
	Feature			-	Good flatness , excellent for machine printing

Note:
1.Storage conditions: constant temperature about 20ºC
2.Avoid the sun, unventilated
3.Valid: not more than 6 month from date of product.
 

PETG  Shrink film

PROPERTY	UNIT	TEST METHOD		TYPICAL VALUE
THICKNESS	um	ASTM D374		50
DENSITY	g/cm3	ASTM D792		1.32
HAZE	%	D1003		4.1
LIGHT TRANSMITTANCE	%	ASTM D1003		90.6
COEFFICIENT OF FRICTION	us	ASTM D1894E		0.5
	uk			0..53
TENSILE STRENGTH	Mpa	ASTM D882	M D	50.2
			TD	243.6
ELONGATION AT BREAK	%	ASTM D882	M D	408
			TD	42.5
SHRINKAGE (In 90ºC water for 10 sec.)	%	ASTM D1204	M D	3
			TD	74